ÇÇ°¡¿Ã¼°¡ ±Ý¼ÓÀÏ ¶§ÀÇ ¹°¸®Àû ¼ºÁú |
|
|
SUBSTANCE |
Density lb/ft3 |
Specific Heat Btu/lb ºF |
Thermal Conductivity Btu in/hr ft2 ºF |
Melting Point ºF (Lowest) |
Latent Heat of Fusion Btu/lb |
Thermal Expansion in/in/ºFX10-6 |
Aluminum 1100-0 | 169 | 0.24 | 1536 | 1190 | 169 | 13.1 |
Aluminum 2024 | 173 | 0.24 | 1344 | 935 | 167 | 12.6 |
Aluminum 30003 | 171.07 | 0.24 | - | 1190 | 167 | - |
Antimony | 413 | 0.049 | 131 | 1166 | 69 | - |
Babbitt-Lead Base |
640 | 0.039 | 165.6 | 470 | - | - |
Babbitt-Tin Base | 462 | 0.071 | 278.4 | 465 | - | - |
Barium |
225 | 0.068 | - | 1562 | - | - |
Beryllium |
113.5 | 0.052 | 1121 | 2345 | - | - |
Bismuth |
610 | 0.031 | 59 | 520 | 22.4 | - |
Boron |
144 | 0.309 | - | 4172 | - | - |
Brass(80-20) | 535 | 0.091 | 82 | 1700 | - | - |
Brass(70-30) |
525 | 0.10 | 672 | 1700± | - | - |
Brass (Yellow) |
529 | 0.096 | 828 | 1710 | - | 11.2 |
Brass, Red | 546.04 | 0.100 | - | 1877 | - | - |
Bronze | 549.50 | 0.104 | - | 1832 | 75 | - |
Bronze(75% Cu, 25% Sn) | 541 | 0.082 | 180 | 1832 | 75 | - |
Cadmium | 540 | 0.055 | 660 | 610 | 23.8 | - |
Calcium |
96.7 | 0.149 | 912 | 1564 | 140 | - |
Carboloy(CementedCarbide) | 875 | 0.052 | 420-636 | 6422 | - | - |
Chromium |
450 | 0.11 | 484 | 2822 | - | - |
Cobalt | 554 | 0.099 | 499 | 2696 | 115.2 | - |
Constantan(55%Cu, 45%Ni) | 555 | 0.098 | - | - | - | - |
Copper | 559 | 0.10 | 2688 | 1981 | 91 | 9.8 |
German Silver | 537 | 0.109 | 168 | 1761 | - | - |
Gold | 1203 | 0.030 | 204 | - | - | - |
Inconel® 800 | 501 | 0.12 | 2028 | 1945 | 29 | 7.9 |
Inconel® 600 | 525 | 0.11 | 97 109 |
2475 2470 |
- - |
7.9 5.8 |
Invar 36% Ni |
506 | 0.126 | 73 | 2600 | - | - |
Lead, Solid | 708.46 | .032 | 240 | 620 | 11.3 | - |
Lead, Liquid | 668.736 | .037 | 108 | - | - | - |
Iron, Cast |
450 | 0.13 | 396 | 2300 | 40 | 6.0 |
Iron,Wrought |
480 | 0.12 | 432 | 2800 | - | - |
Lead |
708 | 0.032 | 240 | 620 | 9.8 | 16.4 |
Linotype |
627 | 0.04 | - | 480 | - | - |
Lithium | 367 | 0.79 | 516 | 367 | 59 | - |
Magnesium |
109 | 0.232 | 1092 | 1202 | - | 14.0 |
Manganese | 463 | 0.115 | 80.6 | 2268 | 116 | - |
Mercury | 844 | 0.033 | 60.8 | 0.38 | 5.0 | - |
Molybdenum | 638 | 0.061 | 980 | 4750 | 126 | 2.9 |
Monel 400 |
551 | 0.11 | 151 | 2370 | - | 6.4 |
Monel 200 | 554.68 | 0.12 | 436 | 2615 | 133 | - |
Muntz Metal(60% Cu, 40%Zn) | 523 | 0.096 | 852 | 1660 | - | - |
Nickel 200 | 554 | 0.11 | 468 | 2615 | 133 | 5.8 |
Nickel Silver | - | - | - | - | - | - |
80%NI-20%CR | 542.59 | 0.095 | - | 1931 | - | - |
Nichrome | 524 | 0.11 | 104.4 | 2550 | - | 7.3 |
Platinum |
1338 | 0.32 | 492 | 3225 | 49 | 4.9 |
Potassium | 750 | 0.058 | 720 | 146 | 26.2 | - |
Rhodium | 776 | 0.059 | 636 | 3570 | - | - |
Silver | 55 | 0.057 | 2904 | 1760 | 38 | 10.8 |
Sodium | 60 | 0.295 | 972 | 207 | 49.5 | - |
Solder(60% Sn, 40% Pb) | 552 | 0.040 | 336 | 420 | 17 | 13.1 |
Solder(50% Sn, 50% Pb) | 540 | 0.045 | 355 | 375 | 28 | - |
Steel, Mild Carbon |
490 | 0.12 | 456 | 2760 | - | 6.7 |
Stainless 304, 316, 321 | 500 | 0.12 | 105.6 |
2550 |
- |
9.6 |
Stainless 430 | 475 | 0.11 | 150 | 2650 | - | 6.0 |
Tantalum | 1036 | 0.036 | 372 | 5425 | - | 3.6 |
Tin | 455 | 0.056 | 432 | 450 | 26.1 | 13.0 |
Tin, Solid | 454.46 | .065 | 455 | 450 | 26.1 | - |
Tin, Liquid | 437.18 | .052 | 218 | - | - | - |
Titanium | 283 | 0.126 | 111.6 | 3035 | - | 4.7 |
Tungsten | 1200 | 0.032 | 1130 | 6170 | 79 | 2.5 |
Type Metal(85% Pb, 15% Sb) | 670 | 0.040 | 180 | 500 | 14 | - |
Uranium | 1170 | 0.028 | 193.2 | 3075 | - | - |
85%Pb 15%Sb | 668.73 | 0.040 | - | 500 | 14 | |
Zinc | 445 | 0.095 | 112-264 | 787 | 43.3 | 22.1 |
Zirconium | 400 | 0.066 | 145 | 3350 | 108 | 3.2 |